In addition to all the basic characteristics of PVC processing aids, foaming regulators have higher molecular weight than general-purpose processing aids and higher melt strength, which can give products more uniform cell structure and lower density. The pressure and torque of PVC melt are increased, so as to effectively increase the cohesion and homogeneity of PVC melt, prevent the combination of bubbles, and obtain uniformly foamed products. Compared with other manufacturers, the foaming regulator produced by Bontag has better fluidity and stronger melt strength.
The pressure and torque of PVC melt are increased, so as to effectively increase the cohesion and homogeneity of PVC melt, prevent the combination of bubbles, and obtain uniformly foamed products. Compared with other manufacturers, the foaming regulator produced by Bontag has better fluidity and stronger melt strength.
| Test items | measurement | Test standard | KF-100 |
| appearance | -- | -- | White powder |
| Surface density | g/cm³ | GB/T 1636-2008 | 0.45±0.10 |
| Trimmings (30 mesh) | % | GB/T 2916 | ≤2.0 |
| Volatile matter | % | ASTM D5668 | ≤1.50 |
| Intrinsic viscosity | -- | GB/T 1632-2008 | 12-16 |
25Kg/bag. The product shall be kept clean during transportation, loading and unloading to prevent exposure to the sun, rain, high temperature and humidity, and to avoid damage to the package. It shall be stored in a cool, dry warehouse without direct sunlight and at a temperature lower than 40oC for two years. After two years, it can still be used after passing the performance inspection.