CPE-135B is mainly used in rubber and PVC products. It is a thermoplastic elastomer made of chlorinated high-density polyethylene; it has excellent elongation at break and excellent toughness; this product is a saturated thermoplastic resin with irregular structure. After mixing with PVC and rubber, it has good extrusion flow.
1. Excellent elongation at break
2. Excellent flame retardant performance
3. Excellent powder fluidity
4. Excellent electrical insulation performance
| Parameter |
Unit |
Test Standard |
CPE-135BA(CM Series Included) |
| Product Appearance |
-- |
Visual Inspection |
White Power |
| Chlorine Content |
% |
-- |
35±2 |
| Apparent Density |
G/Cm³ |
GB/T1636-2008 |
0.50±0.10 |
| Sieve Residue(0.9mm Sieve Hole) |
% |
RK/PG-05-001 |
≤0.2 |
| Volatile Matter |
% |
RK/PG-05-003 |
≤0.4 |
| Residual(750ºC) |
% |
GB/T9345-2008 |
≤0.5 |
| Tensile Strength |
MPa |
GB/T528-2009 |
6-11 |
| Elongation At Break |
% |
GB/T528-2009 |
>800 |
| Hardness Shote A |
-- |
GB/T531-2008 |
≤65 |
| Mooney Viscosity |
ML(1+4)125ºC |
-- |
40-95 |
CPE135B type chlorinated polyethylene is a general term for 35% chlorine content rubber type CM, mainly used in the rubber field. Its processing performance is also very good, and it can produce rubber products with smooth and round surface and flowing matte. It is a rubber product that can replace a variety of rubber in various fields and produce excellent performance.
Type 135B has moderate mooney viscosity, good processing performance and good tensile properties. It is used in the field of wire and cable, hose, and tape. It has excellent heat resistance, oil resistance, flex resistance, flame retardant and other properties, and the conveying pipelines and oil and gas pipelines are better than other synthetic rubbers, especially for the pressure-bearing liquid conveying hose is more unique. It has been used in the production of steel wire hydraulic hoses in foreign countries, and rubber accessories for foreign automobile production are also widely used
135B also has excellent heat resistance, ozone resistance, atmospheric aging resistance, cold resistance, flame retardant, flex resistance, therefore, it is also the preferred choice for the transportation belt production industry, used to produce flame retardant transport belt, heat resistant transport belt, ordinary transport belt, etc., the application of CM will extend the service life of the existing conveyor belt.
The use of other rubber products, in view of the above points of CPE, for rubber parts with special requirements for various uses, CPE can find its application fields, such as automobiles, waterproof materials, rubber parts for ships, rolling stock, etc.
Transportation and packaging
1. 25kg polypropylene packaging bags, or customized packaging according to customer requirements.
2. During the transportation and loading and unloading of products, it should be kept clean to prevent sun and rain, high temperature and humidity, and avoid damage to the packaging. The products should be stored in a cool, dry, no direct sunlight, temperature below 40 °C warehouse, storage period of two years, the products can still be useful if the performance test qualified two years later.